Optimized structural and mechanical properties of borophosphate glass

A series of phosphate glasses composed of (65-x)P₂O₅–15BaO–5Al₂O₃–5ZnO–10Na₂O-xB₂O₃ (x = 0, 2, 4, 6, and 8 mol%) were successfully prepared using the melt-quenching method. The effects of the addition of boron trioxide (B₂O₃) on the physical, structural, and mechanical properties of the glasses were investigated. As the added content of B₂O₃ increased from 0 to 6 mol%, the glass exhibited increased density and transition temperature, and decreased molar volume, indicating optimization of the glass stability. Raman spectroscopy revealed that the introduction of B₂O₃ transformed the glass from a chain structure to a three-dimensional network structure, which enhanced the chemical stability of the glass by the cross-linking of long phosphate chains with boron ions. Regarding the mechanical properties, when the boron content was 6 mol%, the flexural strength of the glass was 41% higher than that of the undoped boron, while the Vickers hardness and Knoop hardness values increased by 20.58% and 7.05%, respectively, and the fracture toughness was slightly decreased. In general, improving the mechanical properties of phosphate glass is of great significance for increasing the applications of this glass.     

基于神经网络算法的井下裂缝诊断与堵漏技术

在钻井过程中，常常钻遇不同宽度的井下地层裂缝。钻遇裂缝时容易发生钻井液漏失现象，甚至发生钻井液失返现象，严重影响了安全、高效钻井。目前裂缝封堵的方法常存在封堵成功率不高、堵漏承压能力低的问题，其中一个重要的原因是对井下地层的裂缝宽度等特征认识不清。基于地层裂缝产生的岩石力学机理，确定影响裂缝宽度关键的6个力学和工程因素，并利用神经网络计算的非线性、大数据特点建立了井下地层裂缝宽度的分析模型，模型包含输入层、输出层和3个隐藏层。通过该模型诊断井下裂缝宽度，提高了计算精度，平均误差仅为2.09%，最大误差为5.88%，解决钻井现场仅凭经验判断裂缝误差较大和依靠成像测井成本较高的问题。同时根据神经网络模型诊断得到的裂缝宽度优化堵漏材料的粒径配比，提高了裂缝内的架桥封堵强度和架桥的稳定性，封堵层的承压能力达到12.8 MPa，反向承压能力达到4.5 MPa。现场堵漏试验最高憋压10 MPa，经过封堵作业后大排量循环不漏，达到了裂缝性地层高效堵漏的目的，堵漏一次成功。      

Finite element analysis of fracture behavior in ceramics: Competition between artificial notch and internal defects under three-point bending

Evaluation of the nonlinear relationship between the surface defect size and fracture strength of ceramics is important for engineering applications. In this study, we aim to predict the apparent nonlinear relationship between the defect size and fracture strength of single-edge notched beams (SENBs) using the finite element method. Specifically, we applied the methodology for predicting fracture strength from microstructure distribution data (relative density, pore size, aspect ratio, and grain size) to a finite element analysis (FEA) model in which the shape and size of the initial defects are defined at notch locations. By reproducing the apparent nonlinearity caused by the competition between the surface and internal defects within the framework of linear elastic fracture mechanics, the effectiveness of the FEA methodology for the evaluation of strength scatter and allowable crack size in ceramics was demonstrated.     

Microstructure and mechanical properties of hot-pressed SiC nanofiber reinforced SiC composites

This study reports on the preparation and mechanical properties of a novel SiC_nf/SiC composite. The single crystal SiC nanofiber(SiC_nf) reinforced SiC ceramic matrix composites (CMC) were successfully fabricated by hot pressing the mixture of β-SiC powders, SiC_nf and Al–B–C powder. The effects of SiC_nf mass fraction as well as the hot-pressing temperature on the microstructure and mechanical properties of SiC_nf/SiC CMC were systematically investigated. The results demonstrated that the 15 wt% SiC_nf/SiC CMC obtained by hot pressing (HP) at 1850 °C with 30 MPa for 60 min possessed the maximum flexural strength and fracture toughness of 678.2 MPa and 8.33 MPa m^1/2, respectively. The nanofibers pull out, nanofibers bridging and cracks deflection were found by scanning electron microscopy, which are believed can strengthen and toughen the SiC_nf/SiC CMC via consuming plenty of the fracture energy. Besides, although the relative density of the prepared SiC_nf/SiC CMC further increased with the sintering temperature rose to 1900 °C, the further coarsend composites grains results in the deterioration of the mechanical properties for the obtained composites compared to 1850 °C.     

Fatigue life improvement of 12Cr1МoV steel by irradiation with Zr+ ion beam

Cyclic tension and bend tests were performed on heat-resistant 12Cr1MoV steel specimens in as-supplied condition as well as after Zr⁺ ion beam surface irradiation. Distinct differences in strain induced relief, as well in cracking pattern of modified surface layer were observed by optical microscopy and interference profilometry. Changes in subsurface layer are characterized by means of nano- and microindentation and fractography of fracture surfaces (with the help of scanning electron microscopy). It is shown that the main influence on mechanical properties is mostly induced by thermal treatment during irradiation rather than formation of a 2 μm thick layer doped with Zr. The differences in deformation behavior may be explained by physical mesomechanics concepts.     

Fatigue in bamboo

This paper describes the results of an experimental programme to determine the fatigue behaviour of bamboo. Bamboo is subjected to cyclic loading, both in the plant itself and subsequently when the material is used in load-bearing applications in the construction industry. However, there is currently no data in the literature describing fatigue in this material. We found that sections of bamboo culm loaded parallel to the culm axis did not undergo fatigue failure: samples either failed on the first loading cycle, or not at all. By contrast, fatigue was readily apparent in samples loaded in compression across the diameter of the culm. The number of cycles to failure increased as the cyclic load range decreased in a manner similar to that found in many engineering materials: fatigue occurred at applied loads as small as 40% of the ultimate strength. Two different species of bamboo were tested and found to have different ultimate strengths but similar high-cycle fatigue strengths. Finite element analysis was used to help understand the progression of fatigue damage and the effect of stress concentration features. Some tentative design rules are proposed to define stress levels for the safe use of bamboo, taking fatigue into account.     

Strengthened interfacial bonding and its effects on fracture mode of TaC ceramics with addition of B

TaC ceramics with 0-0.237 wt% B addition were prepared by hot pressing. The effect of B addition on the phase constitution, interfacial chemistry/bonding and mechanical properties of the TaC ceramics were investigated. Upon B addition, the elimination of O impurity and segregation of B at grain boundaries were evidenced, accompanied by an increase in bonding strength of the TaC grains, to result in a fracture mode change from intergranular to transgranular and a reduced fracture toughness. Addition of excessive B resulted in the formation of TaB₂ and C within TaC ceramics. Further, TaC-TaB₂-SiC composites were prepared by Si addition. Coherent bonding between TaB₂ and TaC was preserved in the TaC-TaB₂-SiC composites, and residual stresses due to thermal expansion mismatch of the different phases increased flexural strength and fracture toughness of the composites.     

Notch radius effect on fracture toughness of ceramics pertinent to grain size

Unlike fracture toughness, the notch fracture toughness of a ceramic is not a constant; rather, it increases with the notch-root radius ρ in a notched specimen. In this study, by analyzing the fracture measurements of eight different notched ceramics with an average grain size G of 3–40 μm, a simple model describing the relation between the notch fracture toughness and fracture toughness is proposed as a function of the relative notch-root radius ρ/G. The normal distribution is incorporated to consider the inevitable scatter in measurements where fracture mechanisms and errors are present. The results demonstrate that the model can effectively predict the quasi-brittle fracture variation trend for ceramics, including the upper and lower bounds, with 96% reliability, from a normal distribution; thus, it can address virtually all of the experimental data. We also determined that the notch fracture toughness approximates the fracture toughness if ρ ≤ G.     

45号钢垫圈断裂的原因分析和改进措施

针对45号钢垫圈在装配后发生断裂的情况,对45号钢垫圈进行断口形貌分析、力学性能分析、化学成分分析和金相组织分析。宏观形貌显示内孔存在加工台阶和明显刀痕,能谱测试发现断裂起始处存在锌元素,金相组织分析确认内孔加工面存在微裂纹。结合加工工艺分析,确认45号钢垫圈的断裂原因,并提出改进措施。